NewsModel Product name S. C. (a) PH Value Viscosity A. P. S.(b) Application
TSR-1050 Triethylene glycol rosin 49~51 5.0~7.0 500MAX(c) 0.1~1.0 Low softening point for low temperature applications and to prevent cold cracking.
ester dispersion Can be used as a co-tackifier for custom softening point development.
TSR-7050 Polyalcohol rosin 49~51 6.0~8.0 150MAX(d) 0.2~1.0 Solvent free, good coating stability in high speed coating, used in acrylate PSA, label,
ester dispersion and VAE pasting glue, increasing initial tack, peel force.
TSR-9050 Rosin Glycerol 49~51 6.0~8.0 150MAX(d) 0.2~1.0 High softening point for higher heat resistance in high temperature applications.
ester dispersion Excellent surface tack for improved adhesion
TSR-5100 Glycerol/ Pentaerythritol 49~51 5.0~7.0 150MAX(d) 0.2 High softening point for higher heat resistance in high temperature applications.
ester dispersion Greatly enhances shear values while maintaining high peel force
TSR-1650 Polymeric rosin glycerol 49~51 5.0~7.0 150MAX(d) 0.2~1.0 Excellent adhesion strength,good compatibility with various latexes or emulsions,
ester dispersion increasing adhesion to non-polarity surface like PP,PE.
TSR-5901 Terpene phenolic 49~51 6.0~8.0 150MAX(d) 0.2~1.0 Use in water borne polymeric latex such as acrylate and CR, NR
resin dispersion latexes polymers to create adhesives.
TSR-5903 Terpene phenolic 49~51 5.0~7.0 300MAX(c) 0.2~1.0 Use in water borne polymeric latex such as acrylate and CR, NR
resin dispersion latexes polymers to create adhesives.
TSR-57035 Terpene phenolic 49~51 5.0~7.0 150MAX(c) 0.2~1.0 Use in water borne polymeric latex such as acrylate and CR, NR
resin dispersion latexes polymers to create adhesives.
TSR-9050TP Terpene resin dispersion 49~51 6.0~8.0 500MAX(d) 0.2 Used in acrylate emulsion, VAE and Natural Rubber latex, increase
initial tack and peel force
a Solid Contain (%)
b Average Particle Size, μm
c BROOKFIELD #2, mpa.s
d BROOKFIELD #1, mpa.s