IntroductionSpecial tackifier dispersion
Model Product name S. C. (a) PH Value Viscosity A. P. S.(b) Application
TSR-1007×55 α-Pinene Terpene 54~56 5.0~8.0 1000MAX(d) 0.2 used in acrylic polymer adhesive, SIS dispersion adhesive, chloroprene rubber
Phenolic resin dispersion latex adhesive, nature rubber latex adhesive and VAE latex adhesive.
TSR-1000×50 Terpene phenolic 49~51 6.0~8.0 100~1400(c) 0.1 MAX Use in water borne polymeric latex such as acrylate chloroprene rubber latex
resin dispersion adhesive, acrylic polymer or carboxylated SBR emulsion.
TSR-5100HH Hydrogenated C5 52~54 6.0~8.0 500MAX(e) 0.2~1.0 used in waterborne PSA, shoe bonding, car interior bonding and packing adhesive
dispersion
dispersion
TSR-5260 Alkyl phenolic dispersion 44~46 5.0~7.0 150MAX(d) 0.2~1.0 use in water-born CR, N.R. increase tack and peel, also help curing
TSR-1068 Terpene phenolic/ 49~51 6.8 150MAX(d) 0.2~1.0 Use in acrylate emulsion, water-born CR to increase anti-yellowing, water
antioxidant dispersion proofness ability, improve peel force and tack.
TSR-5990C Hydrocarbon resin 49~51 5.0~7.0 150MAX(d) 0.2 Used in nature rubber, acrylate and SBR latexes polymers. Greatly enhances
C9 dispersion shear values while maintaining high peel force.
TSR-5920M Hydrocarbon resin 49~51 6.0~8.0 500MAX(e) 0.1max Used in nature rubber, acrylate and SBR latexes polymers. Greatly enhances
C5 dispersion shear values while maintaining high peel force.
a Solid Contain (%)
b Average Particle Size, μm
c BROOKFIELD #3, mpa.s
d BROOKFIELD #1, mpa.s e BROOKFIELD #2, mpa.s